#------------------------------------------------------------------------------ #$Date: 2016-03-20 23:21:50 +0000 (Sun, 20 Mar 2016) $ #$Revision: 178377 $ #$URL: svn://www.crystallography.net/cod/cif/4/00/06/4000626.cif $ #------------------------------------------------------------------------------ # # This file is available in the Crystallography Open Database (COD), # http://www.crystallography.net/ # # All data on this site have been placed in the public domain by the # contributors. # data_4000626 _journal_name_full 'Chemistry of Materials' _journal_paper_doi 10.1021/cm051117v _journal_year 2005 _chemical_formula_sum 'Ga0.25 La O2.37 Ti0.25' _chemical_formula_weight 206.18 _symmetry_cell_setting monoclinic _symmetry_space_group_name_H-M 'P 1 21/c 1' _cell_angle_alpha 90.0 _cell_angle_beta 109.788(8) _cell_angle_gamma 90.0 _cell_formula_units_Z 16 _cell_length_a 8.00474(33) _cell_length_b 11.1123(5) _cell_length_c 11.8456(8) _cell_volume 991.46(11) _cod_depositor_comments ; The following automatic conversions were performed: '_geom_bond_publ_flag' value 'N' changed to 'n' according to '/home/saulius/struct/CIF-dictionaries/cif_core.dic' dictionary named 'cif_core.dic' version 2.4.1 from 2010-06-29 (255 times). Automatic conversion script Id: cif_fix_enum 1527 2010-12-29 10:47:43Z saulius ; _cod_original_sg_symbol_H-M 'P 21/c' _cod_database_code 4000626 loop_ _atom_site_label _atom_site_fract_x _atom_site_fract_y _atom_site_fract_z _atom_site_occupancy _atom_site_thermal_displace_type _atom_site_U_iso_or_equiv _atom_site_symmetry_multiplicity Ga1 0.144(5) 0.195(4) 0.132(4) 0.492(30) Uiso -0.002(17) 4 Ga2 0.720(6) 0.164(4) 0.114(4) 0.508(30) Uiso 0.012(17) 4 La1 0.5222(32) 0.0913(12) 0.7944(11) 1.0 Uiso 0.0170(32) 4 La2 0.025(4) 0.0916(13) 0.7981(14) 1.0 Uiso 0.032(4) 4 La3 0.3365(34) 0.1284(16) 0.4210(12) 1.0 Uiso 0.026(4) 4 La4 0.8436(30) 0.1292(16) 0.4335(11) 1.0 Uiso 0.0134(31) 4 O1 0.753(4) 0.2192(15) 0.7650(16) 1.0 Uiso 0.015(5) 4 O2 0.241(4) 0.2177(21) 0.7547(19) 1.0 Uiso 0.044(9) 4 O3 0.212(5) 0.0378(18) 0.1849(13) 1.0 Uiso 0.031(5) 4 O4 0.110(4) 0.2363(18) 0.9657(16) 1.0 Uiso 0.023(5) 4 O5 0.431(6) 0.2106(19) 0.1183(19) 0.80(5) Uiso 0.030(4) 4 O6 0.616(6) 0.2287(25) 0.9751(20) 1.0 Uiso 0.057(9) 4 O7 0.691(5) 0.0377(19) 0.1556(13) 1.0 Uiso 0.042(6) 4 O8 0.058(4) -0.0045(19) 0.3936(19) 1.0 Uiso 0.027(6) 4 O9 0.576(4) 0.0080(18) 0.3994(16) 1.0 Uiso 0.018(5) 4 Ti1 0.144(5) 0.195(4) 0.132(4) 0.508(30) Uiso -0.002(17) 4 Ti2 0.720(6) 0.164(4) 0.114(4) 0.492(30) Uiso 0.012(17) 4 O10 0.058(8) 0.7464(24) 0.3719(22) 0.66(5) Uiso 0.030(4) 4 loop_ _geom_bond_atom_site_label_1 _geom_bond_atom_site_label_2 _geom_bond_distance _geom_bond_site_symmetry_1 _geom_bond_site_symmetry_2 _geom_bond_publ_flag Ga1 La1 4.05(4) . -1_656 n Ga1 La1 3.82(4) . -2_554 n Ga1 La2 3.91(5) . 1_554 n Ga1 La2 3.66(5) . -1_556 n Ga1 La2 3.42(5) . -2_554 n Ga1 La3 3.33(4) . 1_555 n Ga1 La3 3.88(4) . -2_554 n Ga1 La4 3.36(4) . -2_454 n Ga1 O2 1.71(5) . -2_554 n Ga1 O3 1.87(4) . 1_555 n Ga1 O4 1.95(5) . 1_554 n Ga1 O5 2.37(5) . 1_555 n Ga1 O10 1.70(7) . 2_545 n Ga2 La1 3.67(5) . 1_554 n Ga2 La1 3.79(5) . -1_656 n Ga2 La1 4.09(5) . -2_554 n Ga2 La2 3.45(5) . -1_656 n Ga2 La2 3.81(5) . -2_654 n Ga2 La3 3.90(5) . -2_554 n Ga2 La4 3.59(5) . 1_555 n Ga2 La4 3.50(5) . -2_554 n Ga2 O1 2.15(5) . -2_554 n Ga2 O5 2.38(6) . 1_555 n Ga2 O6 1.73(5) . 1_554 n Ga2 O7 1.53(5) . 1_555 n Ga2 O10 1.96(8) . 2_645 n La1 Ga1 4.05(4) . -1_656 n La1 Ga1 3.82(4) . -2_555 n La1 Ga2 3.67(5) . 1_556 n La1 Ga2 3.79(5) . -1_656 n La1 Ga2 4.09(5) . -2_555 n La1 La1 5.644(4) . 2_646 n La1 La1 5.644(4) . 2_656 n La1 La1 5.398(31) . -1_657 n La1 La2 4.00(4) . 1_555 n La1 La2 4.01(4) . 1_655 n La1 La2 5.360(20) . -1_657 n La1 La3 4.183(20) . 1_555 n La1 La3 3.963(25) . -1_656 n La1 La3 3.958(30) . -2_555 n La1 La4 5.678(27) . 1_455 n La1 La4 5.703(27) . 1_555 n La1 La4 4.063(25) . -1_656 n La1 La4 4.015(23) . -2_555 n La1 O1 2.449(32) . 1_555 n La1 O2 2.56(4) . 1_555 n La1 O3 2.51(4) . -1_656 n La1 O5 3.493(22) . -1_656 n La1 O5 2.950(23) . -2_555 n La1 O6 2.528(25) . 1_555 n La1 O7 4.071(19) . 1_556 n La1 O7 2.45(4) . -1_656 n La1 O9 2.426(25) . -1_656 n La1 Ti1 4.05(4) . -1_656 n La1 Ti1 3.82(4) . -2_555 n La1 Ti2 3.67(5) . 1_556 n La1 Ti2 3.79(5) . -1_656 n La1 Ti2 4.09(5) . -2_555 n La2 Ga1 3.91(5) . 1_556 n La2 Ga1 3.66(5) . -1_556 n La2 Ga1 3.42(5) . -2_555 n La2 Ga2 3.45(5) . -1_656 n La2 Ga2 3.81(5) . -2_455 n La2 La1 4.01(4) . 1_455 n La2 La1 4.00(4) . 1_555 n La2 La1 5.360(20) . -1_657 n La2 La2 5.659(6) . 2_546 n La2 La2 5.659(6) . 2_556 n La2 La2 5.34(4) . -1_557 n La2 La3 5.815(33) . 1_455 n La2 La3 5.822(32) . 1_555 n La2 La3 3.999(29) . -1_556 n La2 La3 3.945(27) . -2_555 n La2 La4 4.085(21) . 1_455 n La2 La4 5.947(21) . 2_646 n La2 La4 4.075(26) . -1_656 n La2 La4 3.984(29) . -2_455 n La2 O1 2.51(4) . 1_455 n La2 O2 2.41(4) . 1_555 n La2 O3 2.44(5) . -1_556 n La2 O4 2.464(22) . 1_555 n La2 O7 2.59(4) . -1_656 n La2 O8 2.348(26) . -1_556 n La2 Ti1 3.91(5) . 1_556 n La2 Ti1 3.66(5) . -1_556 n La2 Ti1 3.42(5) . -2_555 n La2 Ti2 3.45(5) . -1_656 n La2 Ti2 3.81(5) . -2_455 n La2 O10 2.613(33) . -1_566 n La2 O10 3.845(32) . -2_555 n La3 Ga1 3.33(4) . 1_555 n La3 Ga1 3.88(4) . -2_555 n La3 Ga2 3.90(5) . -2_555 n La3 La1 4.183(20) . 1_555 n La3 La1 3.963(25) . -1_656 n La3 La1 3.958(30) . -2_554 n La3 La2 5.822(32) . 1_555 n La3 La2 5.815(33) . 1_655 n La3 La2 3.999(29) . -1_556 n La3 La2 3.945(27) . -2_554 n La3 La3 3.90(4) . -1_656 n La3 La4 3.998(30) . 1_455 n La3 La4 4.012(30) . 1_555 n La3 La4 3.864(23) . -1_656 n La3 O2 2.524(27) . -2_554 n La3 O3 2.818(18) . 1_555 n La3 O4 2.54(4) . -2_554 n La3 O5 4.01(4) . 1_555 n La3 O5 2.835(24) . -2_555 n La3 O6 2.64(5) . -2_554 n La3 O8 2.60(4) . 1_555 n La3 O9 2.42(4) . 1_555 n La3 O9 2.511(26) . -1_656 n La3 Ti1 3.33(4) . 1_555 n La3 Ti1 3.88(4) . -2_555 n La3 Ti2 3.90(5) . -2_555 n La3 O10 4.04(4) . 2_545 n La4 Ga1 3.36(4) . -2_655 n La4 Ga2 3.59(5) . 1_555 n La4 Ga2 3.50(5) . -2_555 n La4 La1 5.703(27) . 1_555 n La4 La1 5.678(27) . 1_655 n La4 La1 4.063(25) . -1_656 n La4 La1 4.015(23) . -2_554 n La4 La2 4.085(21) . 1_655 n La4 La2 5.947(21) . 2_656 n La4 La2 4.075(26) . -1_656 n La4 La2 3.984(29) . -2_654 n La4 La3 4.012(30) . 1_555 n La4 La3 3.998(30) . 1_655 n La4 La3 3.864(23) . -1_656 n La4 La4 3.78(4) . -1_756 n La4 O1 2.523(23) . -2_554 n La4 O4 2.53(4) . -2_654 n La4 O6 2.58(4) . -2_554 n La4 O7 3.261(18) . 1_555 n La4 O8 2.434(31) . 1_655 n La4 O8 2.376(26) . -1_656 n La4 O9 2.44(4) . 1_555 n La4 Ti1 3.36(4) . -2_655 n La4 Ti2 3.59(5) . 1_555 n La4 Ti2 3.50(5) . -2_555 n La4 O10 2.573(27) . -1_666 n O1 Ga2 2.15(5) . -2_555 n O1 La1 2.449(32) . 1_555 n O1 La2 2.51(4) . 1_655 n O1 La4 2.523(23) . -2_555 n O1 O3 2.911(24) . -1_656 n O1 O5 2.69(4) . -2_555 n O1 O7 2.964(27) . -2_555 n O1 Ti2 2.15(5) . -2_555 n O1 O10 2.59(6) . -1_666 n O2 Ga1 1.71(5) . -2_555 n O2 La1 2.56(4) . 1_555 n O2 La2 2.41(4) . 1_555 n O2 La3 2.524(27) . -2_555 n O2 O3 2.826(30) . -2_555 n O2 O5 2.69(5) . -2_555 n O2 Ti1 1.71(5) . -2_555 n O2 O10 2.39(6) . -1_566 n O3 Ga1 1.87(4) . 1_555 n O3 La1 2.51(4) . -1_656 n O3 La2 2.44(5) . -1_556 n O3 La3 2.818(18) . 1_555 n O3 O1 2.911(24) . -1_656 n O3 O2 2.826(30) . -2_554 n O3 O5 2.89(5) . 1_555 n O3 Ti1 1.87(4) . 1_555 n O4 Ga1 1.95(5) . 1_556 n O4 La2 2.464(22) . 1_555 n O4 La3 2.54(4) . -2_555 n O4 La4 2.53(4) . -2_455 n O4 O5 2.61(5) . 1_556 n O4 Ti1 1.95(5) . 1_556 n O4 O10 2.70(6) . 2_546 n O5 Ga1 2.37(5) . 1_555 n O5 Ga2 2.38(6) . 1_555 n O5 La1 3.493(22) . -1_656 n O5 La1 2.950(23) . -2_554 n O5 La3 4.01(4) . 1_555 n O5 La3 2.835(24) . -2_554 n O5 O1 2.69(4) . -2_554 n O5 O2 2.69(5) . -2_554 n O5 O3 2.89(5) . 1_555 n O5 O4 2.61(5) . 1_554 n O5 O6 2.61(6) . 1_554 n O5 O7 2.76(5) . 1_555 n O5 Ti1 2.37(5) . 1_555 n O5 Ti2 2.38(6) . 1_555 n O6 Ga2 1.73(5) . 1_556 n O6 La1 2.528(25) . 1_555 n O6 La3 2.64(5) . -2_555 n O6 La4 2.58(4) . -2_555 n O6 O5 2.61(6) . 1_556 n O6 O7 2.926(31) . 1_556 n O6 Ti2 1.73(5) . 1_556 n O6 O10 2.63(6) . 2_646 n O7 Ga2 1.53(5) . 1_555 n O7 La1 4.071(19) . 1_554 n O7 La1 2.45(4) . -1_656 n O7 La2 2.59(4) . -1_656 n O7 La4 3.261(18) . 1_555 n O7 O1 2.964(27) . -2_554 n O7 O5 2.76(5) . 1_555 n O7 O6 2.926(31) . 1_554 n O7 Ti2 1.53(5) . 1_555 n O8 La2 2.348(26) . -1_556 n O8 La3 2.60(4) . 1_555 n O8 La4 2.434(31) . 1_455 n O8 La4 2.376(26) . -1_656 n O8 O8 2.97(5) . -1_556 n O8 O10 2.781(30) . 1_545 n O9 La1 2.426(25) . -1_656 n O9 La3 2.42(4) . 1_555 n O9 La3 2.511(26) . -1_656 n O9 La4 2.44(4) . 1_555 n Ti1 La1 4.05(4) . -1_656 n Ti1 La1 3.82(4) . -2_554 n Ti1 La2 3.91(5) . 1_554 n Ti1 La2 3.66(5) . -1_556 n Ti1 La2 3.42(5) . -2_554 n Ti1 La3 3.33(4) . 1_555 n Ti1 La3 3.88(4) . -2_554 n Ti1 La4 3.36(4) . -2_454 n Ti1 O2 1.71(5) . -2_554 n Ti1 O3 1.87(4) . 1_555 n Ti1 O4 1.95(5) . 1_554 n Ti1 O5 2.37(5) . 1_555 n Ti1 O10 1.70(7) . 2_545 n Ti2 La1 3.67(5) . 1_554 n Ti2 La1 3.79(5) . -1_656 n Ti2 La1 4.09(5) . -2_554 n Ti2 La2 3.45(5) . -1_656 n Ti2 La2 3.81(5) . -2_654 n Ti2 La3 3.90(5) . -2_554 n Ti2 La4 3.59(5) . 1_555 n Ti2 La4 3.50(5) . -2_554 n Ti2 O1 2.15(5) . -2_554 n Ti2 O5 2.38(6) . 1_555 n Ti2 O6 1.73(5) . 1_554 n Ti2 O7 1.53(5) . 1_555 n Ti2 O10 1.96(8) . 2_645 n O10 Ga1 1.70(7) . 2_555 n O10 Ga2 1.96(8) . 2_655 n O10 La2 2.613(33) . -1_566 n O10 La2 3.845(32) . -2_554 n O10 La3 4.04(4) . 2_555 n O10 La4 2.573(27) . -1_666 n O10 O1 2.59(6) . -1_666 n O10 O2 2.39(6) . -1_566 n O10 O4 2.70(6) . 2_556 n O10 O6 2.63(6) . 2_656 n O10 O8 2.781(30) . 1_565 n O10 Ti1 1.70(7) . 2_555 n O10 Ti2 1.96(8) . 2_655 n